Chemical Research in Chinese Universities ›› 2013, Vol. 29 ›› Issue (3): 589-595.doi: 10.1007/s40242-013-3104-9

• Articles • Previous Articles     Next Articles

Synthesis of Well-defined Long Chain Branched Polyethylene via Anionic Polymerization Combined with Graft-onto Method

LIU Feng1,2, WANG Lu1,2, ZHANG Guang-chun1,2, ZHENG Jun1,2, TANG Tao1   

  1. 1. State Key Laboratory of Polymer Physics and Chemistry, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, P. R. China;
    2. University of Chinese Academy of Sciences, Beijing 100049, P. R. China
  • Received:2013-03-11 Revised:2013-03-20 Online:2013-06-01 Published:2013-05-15
  • Contact: Tao Tang E-mail:ttang@ciac.jl.cn
  • Supported by:

    Supported by the National Natural Science Foundation of China(Nos.51073149, 51233005).

Abstract:

Comb-like polyethylene(PE) was prepared via anionic polymerization combined with “graft-onto” process. The polybutadiene(PB) backbone underwent hydroxylation at 1,2-vinyl groups to obtain a controlled number of hydro- xyl groups along the main chain. After the translation of hydroxyl groups to tosyl groups, a nucleophilic substitution by living anionic PB chains was achieved. The comb PE was finally obtained by the hydrogenation of the obtained unsaturated comb polymer. Since the living anionic polymerization was used to prepare the backbones and the branch chains, molecular weight to molecular weight distribution(Mw/Mn<1.5) can be well-controlled in the final comb polymer, including the average number and length of branches.

Key words: Long chain branching, Polyethylene, Anionic polymerization, Comb-like polymer