Constructing Co(OH)F Nanorod Arrays with a Highly Active CoP/Co(OH)F Interface for Hydrogen Evolution

doi:10.1007/s40242-026-6093-1

Abstract

Abstract: Developing transition metal-based catalysts with high activity and long-term stability has garnered extensive attention for hydrogen evolution reaction (HER). Here, a Co(OH)F nanorod catalyst with a novel CoP/Co(OH)F heterostructure is developed through a simple hydrothermal method and subsequent phosphorization. Notably, the CoP/Co(OH)F shows excellent HER performance, including a low overpotential of 83 mV at 10 mA/cm² and a Tafel slope of 43 mV/dec. Moreover, it also displays outstanding stability for 400 h at a current density of 50 mA/cm². Further analysis reveals that the construction of CoP and Co(OH)F heterojunction interface promotes the electron transfer and further optimizes the adsorption energy of reaction intermediates during HER process. This work provides a new insight to design and construct high-performance heterostructure catalysts for HER.

Key words: Hydrogen evolution reaction, CoP/Co(OH)F, Transition metal, Heterostructure, Phosphorization

LIU Tianpeng, CHEN Hele, GUO Linke, WEN Shiyu, CAO Dong. Constructing Co(OH)F Nanorod Arrays with a Highly Active CoP/Co(OH)F Interface for Hydrogen Evolution[J]. Chemical Research in Chinese Universities, 2026, 42(3): 783-788.

References

[1] Gao Y., Yu H., Wang W., Chi P., Liu S., Rao H., Bian C., Ge J., Joule, 2026, 10, 102337.
[2] Niu Y., Cai H., Wang C., Han C., Tao X., Liu K., Chem. Res. Chinese Universities, 2025, 41, 1201.
[3] Bi X., Zhang W., Tang D., Xin S., Zhao Z., Chem. Res. Chinese Universities, 2025, 41, 101.
[4] Cao D., Gao P., Shen Y., Qiao L., Ma M., Guo X., Cheng D., Adv. Mater., 2025, 37, 2414138.
[5] Xu S., Cen J., Yang G., Si L., Xiao X., Liu H., Chem. Res. Chinese Universities, 2024, 40, 1106.
[6] Li F., NG W.K., Qiao W., Yang Y., Li X., Xi B., Yu Y., Fang J., Li P., Xiong S., Angew. Chem. Int. Ed., 2025, 64, e202511402.
[7] Xia T., Ren Q., Yang J., Li Z., Shao M., Duan X., Chem. Res. Chinese Universities, 2024, 40, 577.
[8] Wang H., Cao W., Sun H., Du X., Wang Y., Li J., Wu L., Liu G., Song S., Angew. Chem. Int. Ed., 2026, 65, e19688.
[9] Ke T., Wang Q., Siniard K., Qiu L., Martins M. L., Cheng Y., Lyu X., Serov A., Ganesan A., Adigun B., Yang Z., Wang T., Dai S., J. Am. Chem. Soc., 2026, 148, 1729.
[10] Jiang H., Wang H., Liu K., Feng Z., Alharthi S., Amin M. A., Lin J., J. Colloid Interface Sci., 2026, 702, 138923.
[11] Qu D., Liang Y., Huang Y., Wan Z., Wang Y., Wang X., Wang J., Zheng Y., Pan J., Cao J., Li C., Electrochim Acta, 2026, 559, 148609.
[12] Meng D., Ran S., Gao L., Zhang Y., San X., Zhang L., Li R., Jin Q., Chem. Res. Chinese Universities, 2024, 40, 490.
[13] Ji P., Zheng D., Jin H., Liao Y., Int. J. Hydrogen Energy, 2024, 57, 473.
[14] Liu T., Liu W., Ma M., Guo L., Cui R., Cheng D., Cao D., Electrochim Acta, 2023, 439, 141721.
[15] Fan H., Wan X., Sun S., Zhou X., Bu X., Ye J., Bai R., Lou H., Chen Y., Gao J., Zhang J., Gao W., Wen D., Adv. Energy Mater., 2025, 15, 2405681.
[16] Guo D., Duan P., Yan Z., An Y., Hu Y., Yao W., Dou Y., Int. J. Hydrogen Energy, 2026, 227, 154601.
[17] Qu D., Zeng S., Yang Z., Wang J., Zheng Y., Pan J., Cao J., Li C., ACS Appl. Nano Mater., 2024, 7, 28669.
[18] Li R., Wang Y., Chen B., Zhang H., Yan C., Xu X., Humayun M., Debecker D.P., Wang C., Int. J. Hydrogen Energy, 2024, 51, 1292.
[19] Gao G., Zhao B., Huang J., Cheng X., Mi H., Abudula A., J. Colloid Interface Sci., 2026, 716, 140314.
[20] Alhakemy A. Z., Kandiel T. A., Chem. Eng. J., 2025, 524, 169547.
[21] Min S., Yang G., Jiao Y., Wang J., Liu Y., Chen Z., Yan H., Fu H., Adv. Funct. Mater., 2026, 36, e14250.
[22] Nan Y., Liu T., Liu W., Cao D., Cheng D., ACS Appl. Mater. Interfaces, 2024, 16, 16309.
[23] Zhao D.-P., Peng Z.-K., S. Wei, Pang Q.-Q., Liu Q.-Y., Liu Z.-Y., Mater. Res. Bull., 2026, 197, 113988.
[24] Alemayehu D. D., Tsai M.-C., Tsai M.-H., Yang C.-C., Chang C.-C., Chang C.-Y., Moges E. A., Lakshmanan K., Nikodimos Y., Su W.-N., Wang C.-H., Hwang B. J., J. Am. Chem. Soc., 2025, 147, 16047.
[25] Liu W., Zhang H., Ma M., Cao D., Cheng D., ACS Appl. Energy Mater., 2022, 5, 10794.
[26] Li D., Li Z., Zou R., Shi G., Huang Y., Yang W., Yang W., Liu C., Peng X., Appl. Catal. B: Environ., 2022, 307, 121170.
[27] Wang D., Zheng Y., Zhao H., Zhu X., Ye D., Yang Y., Chen R., Liao Q., ACS Catal., 2023, 13, 10104.
[28] Zhang H., Liu W., Li Z., Qiao L., Chi K., Guo X., Cao D., Cheng D., Adv. Sci., 2024, 11, 2401398.
[29] Zhang J., Wu Q., Song J., Xu C., Chen S., Guo Y., Nano Energy, 2024, 128, 109923.
[30] Wang B., Chen X., He Y., Liu Q., Zhang X., Luo Z., Kennedy J. V., Li J., Qian D., Liu J., Waterhouse G. I. N., Appl. Catal. B: Environ., 2024, 346, 123741.
[31] Jin M., Liu Y., Qiu L., Kuang X., Hu X., Zhang J., Liu Y., Liu J., Tan C., Li M., Lu S.Y., Chem. Eng. J., 2026, 533, 174633.
[32] Zhao S., Li Z., Guo H.-T., Li J., Liu Z.-L., Wang P.-F., Wang L.-L., Yi T.-F., Adv. Funct. Mater., 2026, 36, e09799.
[33] Feng Y., Gong S., Wang Y., Ban C., Qu X., Ma J., Duan Y., Lin C., Yu D., Xia L., Chen X., Tao X., Gan L., Zhou X., Adv. Mater., 2025, 37, 2412965.
[34] Li S.-L., Zhou H., Zhou Z., Gan L.-Y., Cai F., Zhao Y., Long J., Qiao L., Small Methods, 2025, 9, e01271.
[35] Chen X., Wang X.-T., Le J.-B., Li S.-M., Wang X., Zhang Y.-J., Radjenovic P., Zhao Y., Wang Y.-H., Lin X.-M., Dong J.-C., Li J.-F., Nat. Commun., 2023, 14, 5289.