MxCo3O4/g-C3N4 Derived from Bimetallic MOFs/g-C3N4 Composites for Styrene Epoxidation by Synergistic Photothermal Catalysis

doi:10.1007/s40242-022-2292-6

摘要/Abstract

摘要： Although metal-organic frameworks(MOFs) have been widely reported as precursors for obtaining various porous materials in recent years, the limited MOF types and monofunctional active site of MOF-based catalysts remain to be hard to crack. Herein, bimetallic MOFs, MCo-ZIFs stabilized by graphitized carbon nitride(g-C₃N₄) and their pyrolytic M_xCo₃O₄/g-C₃N₄ hybrids(M=Zn, Cu, Fe, Ni) have been designedly synthesized. The obtained M_xCo₃O₄/g-C₃N₄ hybrids display synergistic photothermal effect from both M_xCo₃O₄ and g-C₃N₄ under visible light irradiation. Significantly, the solution temperature can be heated from room temperature(20℃) to 66℃ after 40 min irradiation. Therefore, the catalytic activity of M_xCo₃O₄/g-C₃N₄ exceeds those of most reported catalysts under mild reaction conditions. The optimal Zn_xCo₃O₄/g-C₃N₄ catalyst realizes 96% conversion and 75% selectivity toward styrene oxide within 20 min. Incredibly, the Cu_xCo₃O₄/g-C₃N₄ could achieve up to 89% selectivity toward styrene oxide. To our knowledge, this is the first report about the novel photothermal effect of ZIFs-derived metal oxides.

关键词: Metal-organic framework, Pyrolysis, Photothermal effect, Styrene epoxidation

Abstract: Although metal-organic frameworks(MOFs) have been widely reported as precursors for obtaining various porous materials in recent years, the limited MOF types and monofunctional active site of MOF-based catalysts remain to be hard to crack. Herein, bimetallic MOFs, MCo-ZIFs stabilized by graphitized carbon nitride(g-C₃N₄) and their pyrolytic M_xCo₃O₄/g-C₃N₄ hybrids(M=Zn, Cu, Fe, Ni) have been designedly synthesized. The obtained M_xCo₃O₄/g-C₃N₄ hybrids display synergistic photothermal effect from both M_xCo₃O₄ and g-C₃N₄ under visible light irradiation. Significantly, the solution temperature can be heated from room temperature(20℃) to 66℃ after 40 min irradiation. Therefore, the catalytic activity of M_xCo₃O₄/g-C₃N₄ exceeds those of most reported catalysts under mild reaction conditions. The optimal Zn_xCo₃O₄/g-C₃N₄ catalyst realizes 96% conversion and 75% selectivity toward styrene oxide within 20 min. Incredibly, the Cu_xCo₃O₄/g-C₃N₄ could achieve up to 89% selectivity toward styrene oxide. To our knowledge, this is the first report about the novel photothermal effect of ZIFs-derived metal oxides.

Key words: Metal-organic framework, Pyrolysis, Photothermal effect, Styrene epoxidation

REN Fengdi, GAO Qiqin, CHEN Yuzhen. M_xCo₃O₄/g-C₃N₄ Derived from Bimetallic MOFs/g-C₃N₄ Composites for Styrene Epoxidation by Synergistic Photothermal Catalysis[J]. 高等学校化学研究, 2022, 38(6): 1361-1367.

REN Fengdi, GAO Qiqin, CHEN Yuzhen. M_xCo₃O₄/g-C₃N₄ Derived from Bimetallic MOFs/g-C₃N₄ Composites for Styrene Epoxidation by Synergistic Photothermal Catalysis[J]. Chemical Research in Chinese Universities, 2022, 38(6): 1361-1367.

参考文献

[1] Tian S., Wang B., Gong W., He Z., Xu Q., Chen W., Zhang Q., Zhu Y., Yang J., Fu Q., Chen C., Bu Y., Gu L., Sun X., Zhao H., Wang D., Li Y., Nat. Commun., 2021, 12, 1;
[2] Punniyamurthy T., Velusamy S., Iqbal J., Chem. Rev., 2005, 105, 2329;
[3] Hu L., Yue B., Wang C., Chen X., He H., Applied Catalysis A:General, 2014, 477, 141;
[4] Liu J., Meng R., Li J., Jian P., Wang L., Jian R., Appl. Catal. B:Environ., 2019, 254, 214;
[5] Liu Y, Tsunoyama H., Akita T., Tsukuda T., Chem. Commun., 2010, 46, 550;
[6] Choudhary V., Dumbre D., Patil N., Uphade B., Bhargava S., J. Catal., 2013, 300, 217;
[7] Zhang D., Li H., Li G., Chen J., Dalton. Trans., 2009,10527;
[8] Patil N., Uphade B., McCulloh D., Bhargava S., Choudhary V., Catal. Commun., 2004, 5, 681;
[9] Hu X., Bai J., Hong H., Li C., Micropor. Mesopor. Mater., 2016, 228, 224;
[10] Moon H., Limb A., Suh M., Chem. Soc. Rev., 2013, 42, 673;
[11] Zhou H., Kitagawab S., Chem. Soc. Rev., 2014, 43, 5415;
[12] Lee J., Farha O., Roberts J., Scheidt K., Hupp S., Chem. Soc. Rev., 2009, 38, 1450;
[13] Liu W., Huang J., Yang Q., Wang S., Sun X., Zhang W., Liu J., Huo F., Angew. Chem. Int. Ed., 2017, 56, 5512;
[14] Yu M., Space B., Franz D., Zhou W., He C., Li L., Krishna R., Chang Z., Li W., Hu T., Bu X., J. Am. Chem. Soc., 2019, 141, 17703;
[15] Bao S., Li J., Guan B., Jia M., Terasaki O., Yu J., Matter, 2020, 3, 498;
[16] Wen Y., Rentería-Gómez Á., Day G., Smith M., Yan T., Ozdemir R., Gutierrez O., Sharma V., Ma X., Zhou H., J. Am. Chem. Soc., 2022, 144, 11840;
[17] Corma A., García H., Llabrés I., Chem. Rev., 2010, 110, 4606;
[18] Gao J., Huang Q., Wu Y., Lan Y., Chen B., Adv. Energy. Sustain. Res., 2021, 2, 2100033;
[19] Wang L., Li S., Chen Y., Jiang H., Small, 2021, 17, 2004481;
[20] Sumida K., Rogow D., Mason J., McDonald T., Bloch E., Herm Z., Bae T., Long J., Chem. Rev., 2012, 112, 724;
[21] Lee Y., Moon H., Cheon Y., Suh M., Angew. Chem. Int. Ed., 2008, 47, 7741;
[22] Jaechul L., Chong Y., Jaheon K., Youngsuk K., Nakeun K., Seo Y., Kimoon K., Tae H., Lee E., Angew. Chem. Int. Ed., 2018, 57, 7869;
[23] Kim E., Siegelman R., Jiang H., Forse A., Lee J., Martell J., Milner P., Falkowski J., Neaton J., Reimer J., Weston S., Long J., Science, 2020, 369, 392;
[24] Zhang Z., Wang H., Li Y., Xie M., Li C., Lu H., Peng Y., Shi Z., Chem. Res. Chinese Universities, 2022, 38(4), 750;
[25] Li S., Gao Y., Li N., Ge L., Bu X., Feng P., Energy Environ. Sci., 2021, 14, 1897;
[26] Kaneti Y., Tang J., Salunkhe R., Jiang X., Yu A., Wu K., Yamauchi Y., Adv. Mater., 2017, 29, 1604898;
[27] Gu Z., Li D., Zheng C., Kang Y., Wöll C., Zhang J., Angew. Chem. Int. Ed., 2017, 56, 6853;
[28] Cao X., Tan C., Sindoro M., Zhang H., Chem. Soc. Rev., 2017, 46, 2660;
[29] Lide O., Tim W., Xiao H., Kapteijn F., Gascon J., Mater. Chem. Front., 2017, 1, 1709;
[30] Ma S., Goenaga G., Call A., Liu D., Chem. Eur. J., 2011, 17, 2063;
[31] Hu M., Reboul J., Furukawa S., Torad N., Ji Q., Srinivasu P., Ariga K., Kitagawa S., Yamauchi Y., J. Am. Chem. Soc., 2012, 134, 2864;
[32] Jiao L., Wan G., Zhang R., Zhou H., Yu S., Jiang H., Angew. Chem. Int. Ed., 2018, 57, 8525;
[33] Shah S., Najam T., Wen M., Zang S., Waseem A., Jiang H., Small. Struct., 2022, 3, 2100090;
[34] Jiao L., Zhang R., Wan G., Yang W., Wan X., Zhou H., Shui J., Yu S., Jiang H., Nat. Commun., 2020, 11, 2831;
[35] Srinivas G., Krungleviciute V., Guo Z., Yildirim T., Energy Environ. Sci., 2014, 7, 335;
[36] Kung C., Goswami S., Hod I., Wang T., Duan J., Farha O., Hupp J., Acc. Chem. Res., 2020, 53, 1187;
[37] Jiang H., Liu B., Lan Y., Kuratani K., Akita T., Shioyama H., Zong F., Xu Q., J. Am. Chem. Soc., 2011, 133, 31,11854;
[38] Zhang T., Lin W., Chem. Soc. Rev., 2014, 43, 5982;
[39] Liu B., Shioyama H., Akita T., Xu Q., J. Am. Chem. Soc., 2008, 130, 5390;
[40] Wang F., Li C., Chen H., Jiang R., Sun L., Li Q., Wang J., Yu J., Yan C., J. Am. Chem. Soc., 2013, 135, 5588;
[41] Song S., Wang X., Li S., Wang Z., Zhu Q., Zhang H., Chem Sci., 2015, 6, 6420;
[42] Zhang W., Wu Z., Jiang H., Yu S., J. Am. Chem. Soc., 2014, 136, 14385;
[43] Zhi G., Yu X., Zhao D., Chem. Soc. Rev., 2021, 50, 4629;
[44] Tang J., Salunkhe R., Liu J., Torad N., Imura M., Furukawa S., Yamauchi Y., J. Am. Chem. Soc., 2015, 137, 1572;
[45] Xiao C., Lin Y., Zhang J., Chen X., Angew. Chem. Int. Ed., 2006, 45, 1557;
[46] Li B., Liu J., Liu Q., Chen R., Zhang H., Yu J., Song D., Li J., Zhang M., Wang J., Appl. Surf. Sci., 2019, 475, 700;
[47] Chen Y., Wang C., Wu Z., Xiong Y., Xu Q., Yu S., Jiang H., Adv. Mater., 2015, 27, 5010;
[48] Zheng F., Yang Y., Chen Q., Nat. Commun., 2014, 5, 5261;
[49] Zhang S., Guan B., Lu X., Xi S., Du Y., Lou X., Adv. Mater., 2020, 32, 2002235;
[50] Rabani I., Zafar R., Subalakshmi K., Kim H., Bathula C., Seo Y., J. Hazard. Mater., 2021, 407, 124360;
[51] Su T., Lu G., Sun K., Zhang M., Cai C., Catal. Sci. Technol., 2022, 12, 216;
[52] Han Y., Li J., Zhang T., Qi P., Li S., Gao X., Zhou J., Feng X., Wang B., Chem. Eur. J., 2018, 24, 1651;
[53] Guo J., Wan Y., Zhu Y., Zhao M., Tang Z., Nano. Res., 2021, 14, 2037;
[54] Hao Y., Chen L., Li J., Guo Y., Su X., Shu M., Zhang Q., Gao W., Li S., Yu Z., Gu L., Feng X., Yin A., Si R., Zhang Y., Wang B., Yan C., Nat. Commun., 2021, 12, 2682;
[55] Jain P., Huang X., El-Sayed I., El-Sayed M., Acc. Chem. Res., 2008, 41, 1578;
[56] Yang Q., Xu Q., Yu S., Jiang H., Angew. Chem. Int. Ed., 2016, 55, 3785;
[57] Linic S., Aslam U., Boerigter C., Morabito M., Nat. Mater., 2015, 14, 567;
[58] Wang Y., Liu L., Ma T., Zhang Y., Huang H., Adv. Funct. Mater., 2021, 31, 2102540;
[59] Ismael M., J. Alloy. Compd., 2020, 846, 156446;
[60] Huang T., Fu Y., Peng Q., Yu C., Zhu J., Yu A., Wang X., Appl. Surf. Sci., 2019, 480, 888;
[61] Liu J., Wang H., Antonietti M., Chem. Soc. Rev., 2016, 45, 2308;
[62] Liu X., Yang W., Chen L., Liu Z., Long L., Wang S., Liu C., Dong S., Jia J., ACS Appl. Mater. Inter., 2020, 12, 4463;
[63] Bi L., Xu D., Zhang L., Lin Y., Wang D., Xie T., Phys. Chem. Chem. Phys., 2015, 17, 29899;
[64] Wang Y., Wang X., Antonietti M., Angew. Chem. Int. Ed., 2012, 51, 68;
[65] Yang L., Liu J., Yang L., Zhang M., Zhu H., Wang F., Yin J., Renew. Energ., 2020, 145, 691;
[66] Liu D., Chen D., Li N., Xu Q., Li H., He J., Lu J., Small, 2019, 15, 1902291;
[67] Gu W., Hu L., Li J., Wang E., ACS. Appl. Mater. Inter., 2016, 8, 35281;
[68] Wang R., Yan T., Han L., Chen G., Li H., Zhang J., Shi L., Zhang D., J. Mater. Chem. A, 2013, 6, 5752;
[69] Zhu Z., Chen C., Wu R., J. Chin. Chem. Soc., 2020, 67, 1654;
[70] Luo D., Liu S., Liu J., Zhao J., Miao C., Ren J., Ind. Eng. Chem. Res., 2018, 57, 11920;
[71] Muniandy L., Adam F., Mohamed A., Iqbal A., Rahman N., Appl. Surf. Sci., 2017, 398, 43;
[72] Cao S., Low J., Yu J., Jaroniec M., Adv. Mater., 2015, 27, 2150;
[73] Zhou Q., Zhang Z., Cai J., Liu B., Zhang Y., Gong X., Sui X., Yu A., Zhao L., Wang Z., Chen Z., Nano Energy, 2020, 71, 104592;
[74] Banerjee R., Phan A., Wang B., Knobler C., Furukawa H., O'Keeffe M., Yaghi O., Science, 2008, 319, 939;
[75] Wang P., Zhang X., Shi R., Zhao J., Yuan Z., Zhang T., Energy Fuels, 2022, 36, 11627;
[76] Chen H., Shi R., Zhang T., Molecules, 2021, 26, 7552;
[77] Li Y., Li R., Li. Z, Xu Y., Yuan H., Ouyang S., Zhang T., Solar RRL, 2022, 6, 2200493;
[78] Wang Y., Wu X., Shao B., Yang X., Owens G., Xu H., Sci. Bull., 2020, 65, 1380;
[79] Bastienne B., Patricia A., Feiters M., Nolte R., J. Chem. Soc., Dalton Trans., 1998,2241;
[80] Gansäuer A., Lauterbach T., Narayan S., Angew. Chem. Int. Ed., 2003, 42, 5556

M_xCo₃O₄/g-C₃N₄ Derived from Bimetallic MOFs/g-C₃N₄ Composites for Styrene Epoxidation by Synergistic Photothermal Catalysis

M_xCo₃O₄/g-C₃N₄ Derived from Bimetallic MOFs/g-C₃N₄ Composites for Styrene Epoxidation by Synergistic Photothermal Catalysis

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	LIN Tian, WANG Haowu, CUI Chengqian, LIU Wei, LI Guodong. Recent Advances on Confining Noble Metal Nanoparticles Inside Metal-Organic Frameworks for Hydrogenation Reactions[J]. 高等学校化学研究, 2022, 38(6): 1309-1323.
[2]	WANG Yuda, ZULPYA Mahmut, ZHANG Xinyao, XU Shihan, SUN Jiao, DONG Biao. Recent Advances of Metal-Organic Frameworks-based Nanozymes for Bio-applications[J]. 高等学校化学研究, 2022, 38(6): 1324-1343.
[3]	WANG Yitong, MENG Fanchen, SU Ruifa, SUN Changrui, HAN Qianqian, ZHANG Weina, ZHANG Suoying. Synergistic Catalysis of Enzymes and Biomimetic MOFs:Immobilizing Cyt c on Two-dimensional MOFs to Enhance the Performance of Peroxidase[J]. 高等学校化学研究, 2022, 38(6): 1356-1360.
[4]	CHEN Liquan, LI Dawei, REN Jinghan, LI Yameng, GAO Dong, XING Chengfen. Side Chain Functional Conjugated Porous Polymers for NIR Controlled Carbon Dioxide Adsorption and Release[J]. 高等学校化学研究, 2022, 38(6): 1467-1474.
[5]	PANG Kuan, XUE Huan, LIU Haixiong, SUN Jing, LIU Tianfu. Chelating Metal Ions in a Metal-Organic Framework for Constructing a Biomimetic Catalyst Through Post-modification[J]. 高等学校化学研究, 2022, 38(6): 1542-1546.
[6]	WANG Wenyang, LIU Hanlin, YANG Caoyu, FAN Ting, CUI Chengqian, LU Xiaoquan, TANG Zhiyong, LI Guodong. Coordinating Zirconium Nodes in Metal-Organic Framework with Trifluoroacetic Acid for Enhanced Lewis Acid Catalysis[J]. 高等学校化学研究, 2022, 38(5): 1301-1307.
[7]	LI Jingkang, JIANG Yanxiao, YANG Jukun, SUN Ying, MA Pinyi, and SONG Daqian. Fabrication of the Metal-Organic Framework Membrane with Excellent Adsorption Properties for Paraben Based on Micro Fibrillated Cellulose[J]. 高等学校化学研究, 2022, 38(3): 790-797.
[8]	ZHANG Ziqi, WANG Hanbo, LI Yuxin, XIE Minggang, LI Chunguang, LU Haiyan, PENG Yu, and SHI Zhan. Confined Pyrolysis Synthesis of Well-dispersed Cobalt Copper Bimetallic Three-dimensional N-Doped Carbon Framework as Efficient Water Splitting Electrocatalyst[J]. 高等学校化学研究, 2022, 38(3): 750-757.
[9]	QIAO Junyi, LIU Xinyao, ZHANG Lirong, LIU Yunling. Self-assembly of 3p-Block Metal-based Metal-Organic Frameworks from Structural Perspective[J]. 高等学校化学研究, 2022, 38(1): 31-44.
[10]	LI Hengbo, WANG Kuikui, WU Mingyan, HONG Maochun. A Cage-based Porous Metal-Organic Framework for Efficient C₂H₂ Storage and Separation[J]. 高等学校化学研究, 2022, 38(1): 82-86.
[11]	YOU Dongyu, ZHAO Yujuan, YANG Weiting, PAN Qinhe, LI Jiyang. Metal-Organic Framework-based Wood Aerogel for Effective Removal of Micro/Nano Plastics[J]. 高等学校化学研究, 2022, 38(1): 186-191.
[12]	YU Xinyue, ZHONG Yao, SUN Yu, CHEN Yanwei. Controllable Preparation of Plasmonic Gold Nanostars for Enhanced Photothermal and SERS Effects[J]. 高等学校化学研究, 2020, 36(6): 1284-1291.
[13]	LEI Huijin, ZHANG Xinlu, JIN Jiongke, WANG Shuhua, DING Shunmin, ZHANG Ning, CHEN Chao. Highly Uniform Alkali Doped Cobalt Oxide Derived from Anionic Metal-Organic Framework: Improving Activity and Water Tolerance for CO Oxidation[J]. 高等学校化学研究, 2020, 36(5): 946-954.
[14]	WEN Jinguli, LI Yuwen, GAO Junkuo. Two-dimensional Metal-Organic Frameworks and Derivatives for Electrocatalysis[J]. 高等学校化学研究, 2020, 36(4): 662-679.
[15]	LEI Jia, ZENG Mengqi, FU Lei. Two-dimensional Metal-Organic Frameworks as Electrocatalysts for Oxygen Evolution Reaction[J]. 高等学校化学研究, 2020, 36(4): 504-510.